Hemi Metals, located in Hamilton, New Zealand, is a reliable manufacturer and supplier of top-notch Stainless Steel 416 Bars and Rods, perfect for precision machining and demanding industrial applications. SS 416 is a free-machining martensitic stainless steel designed to provide outstanding machinability, solid mechanical strength, and decent corrosion resistance. With a focus on strict dimensional accuracy, controlled metallurgical quality, and a smooth surface finish, these bars and rods guarantee high productivity and consistent performance. Hemi Metals caters to various industries, including automotive, industrial machinery, oil & gas, and precision engineering, where accuracy, speed, and durability are crucial.
Stainless Steel 416 is composed of about 12–14% chromium, with a carefully controlled carbon content and added sulfur to boost machinability. While the sulfur enhances cutting performance, it does slightly compromise corrosion resistance compared to SS 410. Typically, SS 416 bars and rods achieve tensile strength between 500–700 MPa after heat treatment, showcasing good hardness and moderate ductility. This material is magnetic, responds well to hardening and tempering, and maintains excellent dimensional stability during machining, ensuring reliable mechanical performance.
Specification : ASTM A276, A479 / ASME SA276, SA479
Standard : EN, DIN, JIS, ASTM, BS, ASME, AISI
Round Bars : Outside Diameter in the range of 4mm to 500mm
Bright Bars : Outside Diameter in the range of 4mm to 100mm
Hex Bars : 18mm – 57mm (11/16″ to 2-3/4″)
Square Bars : 18mm – 47mm (11/16″ to 1-3/4″)
Finish : Black, Bright Polished, Rough Turned, NO.4 Finish, Matt Finish, BA Finish
Length : 1 to 6 Meters, Custom Cut Lengths
Form : Round, Square, Hex (A/F), Rectangle Etc.
| Grade | C | Mn | Si | P | S | Cr | Mo | Ni | Fe |
| SS 416 | 0.15 max | 1.25 max | 1.0 max | 0.06 max | 0.15 min | 14.00 – 12.00 | 0.6 | – | – |
| Density | Melting Point | Tensile Strength | Yield Strength (0.2%Offset) | Elongation |
| 8.0 g/cm3 | 1454 °C (2650 °F) | Psi – 75000 , MPa – 515 | Psi – 30000 , MPa – 205 | 35 % |
| STANDARD | WERKSTOFF NR. | UNS | JIS | EN | BS |
| SS 416 | 1.4005 | S41600 | SUS 416 | X12CrS13 | 416S21 |
Stainless Steel 416 is a martensitic stainless steel with a higher level of sulfur and carbon content, which enhances its machinability compared to other stainless steels. This alloy offers improved strength and hardness while still maintaining a good level of corrosion resistance, making it suitable for precision machining.
Yes, Stainless Steel 416 can be heat-treated to increase its hardness. It can be hardened through a quenching and tempering process, which improves its strength, making it ideal for applications that require high wear resistance.
Stainless Steel 416 Bars and Rods find extensive use in applications that demand superior machinability, solid strength, and moderate corrosion resistance. They are commonly utilized in shafts, valve components, fasteners, pump parts, spindles, bushings, couplings, and precision-machined components. In sectors like automotive, oil & gas, and industrial machinery, SS 416 bars and rods are essential for high-speed production parts and rotating mechanical assemblies. They are also used in tooling, fittings, and general engineering fabrications. With their remarkable machinability, strength, and cost-effectiveness, they ensure high productivity across various applications.
We provide products that come with both mill test certificates and third-party test certificates, ensuring the highest standards of quality and compliance.
Hemi Metals is a leading manufacturer, supplier, and exporter of high-quality bars, rods, and forgings, catering to various industries in Hamilton New Zealand
Copyright 2024 Hemi Metals. All rights reserved